美国苏威PVDF 6008/0001氟乙烯耐高温耐腐
卓越的耐化学性，能抵抗多种侵蚀性液体和溶剂。
表面光滑，可防污
良好的抗渗透性
注塑成型级
卓越的强度和尺寸稳定性
良好的颜色稳定性
3M™ Dyneon™ 氟塑料聚偏氟乙烯 6008/0001是适合多个行业各种应用领域的理想产品，其固有的纯度和耐化学性能抵抗各种侵蚀性液体和溶剂。采用各种常规热塑性转换技术来轻松加工处理均聚物聚偏氟乙烯。
采用各种常规热塑性转换技术来轻松加工处理聚偏氟乙烯 6008/0001，是适合于挤压的理想产品，表现出卓越的尺寸稳定性、抗磨性和高强度。当温度逐步升高时，聚偏氟乙烯 6008/0001能维持其机械性能。典型应用：聚偏氟乙烯 6008/0001 是适于挤压的理想材料。
3M Dyneon™ PVDF 6008/0001 Polyvinylidene Fluoride
PVDF
3M Dyneon™
产品说明：
Polyvinylidene Fluoride (PVDF) is ideal for multiple applications across a wide array of industries. Widely used in the chemical process industry, wire and cable industry, semiconductor industry, and oil and gas industry, PVDF is also gaining recognition in automotive, building, electronics, pharmaceutical and batteries. 3M™ Dyneon™ PVDF 6008/0001 is easily processed under a variety of conventional thermoplastic conversion techniques, being particularly suitable for extrusion. PVDF 6008/0001 is inherently pure and chemically resistant against a variety of aggressive fluids and solvents. PVDF 6008/0001 exhibits excellent dimensional stability, abrasion resistance and high strength, and maintains its mechanical properties at elevated temperature.
Excellent chemical resistance to a variety of aggressive fluids and solvents
Good permeation resistance
Smooth, anti-fouling surfaces
Injection molding grade
Excellent strength and dimensional stability
Good color stability
Information provided by Dyneon, A 3M Company
物性信息：
| 密度 | 1.78 g/cc | 0.0643 lb/in³ | ISO 1183 |
| 吸水率 | <= 0.040 % | <= 0.040 % | 24 hr @ 23°C; ISO 62 (method 1) |
| Melt Index of Compound | 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 8.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| 24 g/10 min @Load 5.00 kg, Temperature 230 °C | 24 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 |
| 抗张强度(断裂) | 55.0 MPa | 7980 psi | 50mm/min; ASTM D638 |
| 抗张强度(屈服) | 42.0 MPa | 6090 psi | 50mm/min; ASTM D638 |
| 伸长率 (断裂) | 35 % | 35 % | 50mm/min; ASTM D638 |
| 屈服伸长率 | 7.0 % | 7.0 % | 50mm/min; ASTM D638 |
| 弯曲模量 | 2.20 GPa | 319 ksi | 2mm/min; ASTM D790 |
| 熔融温度 | 174 °C | 345 °F | ASTM D3418 |
| 载荷下热变形温度(0.46 MPa) | 147 °C | 297 °F | ASTM D648 |
| 载荷下热变形温度(1.8 MPa) | 112 °C | 234 °F | |
| 可燃性(UL94) | V-0 | V-0 | |
| 极限氧指数 | 44 % @Thickness 3.00 mm | 44 % @Thickness 0.118 in | Sheet; ASTM D2863 |
| 流量 | 3.0 % | 3.0 % |